PLA Resin REVODE101

Transparency, gloss and mechanical properties similar to PET PET, the toughness is poor, easy to color, easy printing, mainly used for laminating, blend film etc.....

Send InquiryChat Now

PLA takes annually renewable resources – corn, cassava and other plants as raw material. After fermentation by microorganisms, lactic acid will be extracted, then PLA will be produced through a process of refining, dehydration polymerization, high temperature pyrolysis and final polymerization. PLA has excellent biodegradable property. After disposal, within one year, it can be degraded into carbon dioxide and water by microorganisms in the soil, and do no harm to our environment. PLA is a kind of aliphatic polyester with basic characteristics of general micromolecule materials. PLA has good machanical properties, low shrinkage, and is competent to the application of most synthetic plastics, also it's widely used in the production of package materials, disposable tableware, household electrical appliance shell, fiber, 3D supplies etc.

Because PLA derives from renewable plant resoures but not the petroleum-based traditional plastics, so it can truely realize energy-saving and enviromental protection, and PLA is considered to be the most promising new "ecological material".

Performance indicator reference

ITEM

UNIT

REFERENCE INDEX

Appearance

White or yellow cylindrical granules

Particle Diameter

mm

2~4

Density

g/cm3

1.25±0.05

Monomer

%

≤1

Melt Index(190℃ 2.16kg)

g/10min

1~30

Glass Transition Temperature

58~60

Melting Point

~160

Tensile Strength at Break

MPa

~50

Tensile Modulus

GPa

3.5~6.0

Impact Strength

J/m

10~13

Mechanical performance comparison


Item

Unit

PP

GPPS

PET

PLA

Density

g/cm3

0.90—0.91

1.04—1.09

1.3—1.4

1.25

Melt index

g/10min

0.2—20

1.5—30

1—30

Tensile strength

MPa

29.6—35

≥58.8

≥60

≥50

Elongation

%

200—700

1.0—2.5

30—70

≥5

Transmittance

%

85—88

88—92

90—92

90—95

 Characteristics of REVODE101


PLA Resin REVODE101

Rest method

Physical property

Density(g/cm3

1.25±0.05

GB/T1033-1986

Melt index,g/10min(190℃,2.16Kg

2-10

GB/T3682-2000

Melting point(℃)

140-155

GB/T19466.3-2004

Glass transition temperature(℃)

56-60

GB/T19466.3-2004

Mechanical property

Tensile strength(Mpa)≥

50

GB/T1040-1992

Elongation at break(%)≥

3.0

GB/T1040-1992

Impact strength(KJ/m2,Izod)≥

1~3

GB/T1043-1992

 

  Application of REVODE101:
  REVODE101 Used for processing a variety of products, and its applications in the expanding. It is suitable for processing products including a cup of cold water, fruit packing box, salad, fruit plate, egg holder, electronic tray, bubble shell, IC card, a cup cover, cake cover, pipe, geonet.